ASTM A832/A832M alloy steel plates for pressure vessels

ASTM A832 is a kind of Cr-Mo-V alloy steel plates material used to fabric pressure vessels. A832 is divided into three grades or levels : A832 Grade 21V, A832 Grade 22V, A832 Grade 23V.

Standard: ASTM A832/A832M
Steel Grade : A832 Grade 21V, A832 Grade 22V, A832 Grade 23V
Thickness :3mm -500mm
Width :1000mm-4000mm
Length :1000mm-18000mm
MOQ: 1 PC
Delivery time : 10-40 days (Production)
Stock : Unavailable
MTC: Available
Payment Term : T/T or L/C At sight .

ASTM A832 steel chemical composition :

Composition	Type	A832 Gr. 21V	A832 Gr. 22V	A832 Gr. 23V
C	Heat analyse	0.10~0.15	0.11~0.15	0.10~0.15
C	Product analyse	0.08~0.18	0.09~0.18	0.08~0.18
Mn	Heat analyse	0.30~0.60	0.30~0.60	0.30~0.60
Mn	Product analyse	0.25~0.66	0.25~0.66	0.25~0.66
P ≤	Heat analyse	0.025	0.015	0.025
P ≤	Product analyse	0.025	0.020	0.025
S ≤	Heat analyse	0.025	0.010	0.010
S ≤	Product analyse	0.025	0.015	0.010
Si ≤	Heat analyse	0.10	0.10	0.10
Si ≤	Product analyse	0.13	0.13	0.13
Cr	Heat analyse	2.75~3.25	2.00~2.50	2.75~3.25
Cr	Product analyse	2.63~3.37	1.88~2.62	2.63~3.37
Mo	Heat analyse	0.90~1.10	0.90~1.10	0.90~1.10
Mo	Product analyse	0.85~1.15	0.85~1.15	0.85~1.15
V	Heat analyse	0.20~0.30	0.25~0.35	0.20~0.30
V	Product analyse	0.18~0.33	0.23~0.37	0.18~0.33
Ti	Heat analyse	0.015~0.035	≤ 0.030	-
Ti	Product analyse	0.005~0.045	≤ 0.035	-
B	Heat analyse	0.001~0.003	≤ 0.0020	-
B	Product analyse	-	-	-
Cu ≤	Heat analyse	-	0.20	-
Cu ≤	Product analyse	-	0.23	-
Ni ≤	Heat analyse	-	0.25	-
Ni ≤	Product analyse	-	0.28	-
Nb ≤	Heat analyse	-	0.07	0.015~0.070
Nb ≤	Product analyse	-	0.08	0.010~0.075
Ca ≤	Heat analyse	-	0.015	0.0005~0.0150
Ca ≤	Product analyse	-	0.020	-

ASTM A832 /A832M Abstract :
ASTM A832 covers the specific chromium-molybdenum-vanadium alloy steel plates intended primarily for the fabrication of welded pressure vessels. The steel shall be killed and shall conform to the fine grain size requirement. All plates shall undergo normalization and tempering. Heat and product analyses shall be conducted and the steel shall conform to the prescribed chemical composition in carbon, manganese, phosphorus, sulfur, silicon, chromium, molybdenum, vanadium, titanium, boron, and copper. Tension and notch toughness testing shall be performed on the material and shall meet the required mechanical properties such as tensile strength, yield strength, and elongation.